AIREX® T10 is a closed-cell, thermoplastic and recyclable polymer foam with a very homogeneous cell structure, high mechanical properties and an outstanding price / performance ratio.

It has an extraordinary resistance to fatigue, is chemically stable, UV-resistant and has negligible water absorption. It is thermally stable during high temperature processing and post curing without after expansion or outgassing. T10 is designed for easy use with all resin systems and processing technologies.

AIREX® T10 is ideally suited for high volume applications of lightweight sandwich structures subjected to static and dynamic loads and/or exposed to elevated temperatures during manufacturing.

AIREX® T10.100 AIREX® T10.110
Data sheet Adobe_Reader_v9.0_icon
Density, kg/m³ 100 110
Compressive strength, MPa 1.5 1.9
Compressive modulus, MPa 100 125
Tensile strength, MPa 2.0 2.3
Tensile modulus, MPa 130 160
Shear strength, MPa 1.05 1.15
Shear modulus, MPa 33 37
Shear elongation at break, % 15 15
Long term thermal stability, °C 100 100
Maximum processing temperature, °C 150 150