AIREX® T92 is a closed-cell, thermoplastic and recyclable polymer foam with very good mechanical properties and an outstanding price / performance ratio.

It has an extraordinary resistance to fatigue, is chemically stable, UV-resistant and has negligible water absorption. It is thermally stable during high temperature processing and post curing without after expansion or outgassing. T92 is designed for easy use with all resin systems and processing technologies.

AIREX® T92 is ideally suited as a core material for a wide variety of lightweight sandwich structures subjected to static and dynamic loads and/or exposed to elevated temperatures during manufacturing.

AIREX® T92.60 AIREX® T92.80 AIREX® T92.100 AIREX® T92.130 AIREX® T92.200 AIREX® T92.320
Data sheet Adobe_Reader_v9.0_icon
Density, kg/m³ 65 85 100 135 210 320
Compressive strength, MPa 0.8 1.3 1.75 2.4 3.5 7.1
Compressive modulus, MPa 50 75 90 140 180 280
Tensile strength, MPa 1.5 1.9 2.3 2.6 3.1 4.5
Tensile modulus, MPa 85 90 110 175 230 420
Shear strength, MPa 0.50 0.72 0.90 1.30 2.00 3.50
Shear modulus, MPa 13 22 26 34 55 110
Shear elongation at break, % 25 30 20 12 6 5
Long term thermal stability, °C 100 100 100 100 100 100
Maximum processing temperature, °C 150 150 150 150 150 150